Non-Destructive Hardness Testing

Nondestructive testing (NDT) or Nondestructive evaluation (NDE) is a method of materials testing to assess the characteristics of a component without altering or destroying it. NDT is important in the materials testing industry where quick, dependable information on finished or raw material is needed. This may occur during the production stage, during the service life of a material or product, or as a diagnostic tool in the event of material failure.

NDT is contrary to destructive testing such as stress or bend testing where critical material properties are determined through achieving specimen failure. While destructive testing is intrinsically more revealing; it also is costly to a manufacturing operation due to material loss and, for obvious reasons, it is not suitable for in service material testing.

Application uses for NDT cover a comprehensive range of material and industries such as automotive, aerospace, construction, and a multitude of manufacturing types. A classic example of NDT at work is testing for weld defects at manufacture and periodically during service life of the welded material. Other typical applications include crack detection in aircraft skins, surface flaws in pipes or bar, and evaluation of heat treating of product.

NDT has also become a valuable tool in the research and development field where quick, reliable data can provide vital information on materials. Typical types and method of NDT include Ultrasonics, Eddy Current, Rebound, and Ultrasonic Contact Impedance. Hardness testing by diamond or ball indentation is also, sometimes arguably, considered a form of NDT, as in most cases the material is only indiscernibly effected. The force applied in a hardness test correlated either with the depth of indent or with area of indent provides a measurement of hardness. Typically the properties and usefulness of the material is not compromised. Microhardness testing is the best example of a nondestructive hardness test. Some of the more common NDT test types are described below.

Common Nondestructive Tests

Ultrasonic Testing

Ultrasonic Testing (UT) uses high frequency sound energy to evaluate a variety of materials to produce vital information. It’s typically used for flaw detection, dimensional measurements and surface thickness. A typical system would include a pulser/receiver, transducer, and display device. The pulser produces high voltage electrical pulses to the transducer whish in turn generate ultrasonic energy. The energy is introduced to and flows through the test piece in the form of waves . Flaws are detected as a discontinuity on the wave path, the resultant electrical signal is displayed on the display device. UT is one of the more widely used forms NDT and has several advantages including minimal material preparation, instant results, high accuracy, and access to only a single side of the workpiece. UT is used on steels, concrete, wood, and composites.

NDT is contrary to destructive testing such as stress or bend testing where critical material properties are determined through achieving specimen failure. While destructive testing is intrinsically more revealing; it also is costly to a manufacturing operation due to material loss and, for obvious reasons, it is not suitable for in service material testing.

Application uses for NDT cover a comprehensive range of material and industries such as automotive, aerospace, construction, and a multitude of manufacturing types. A classic example of NDT at work is testing for weld defects at manufacture and periodically during service life of the welded material. Other typical applications include crack detection in aircraft skins, surface flaws in pipes or bar, and evaluation of heat treating of product.

NDT has also become a valuable tool in the research and development field where quick, reliable data can provide vital information on materials. Typical types and method of NDT include Ultrasonics, Eddy Current, Rebound, and Ultrasonic Contact Impedance. Hardness testing by diamond or ball indentation is also, sometimes arguably, considered a form of NDT, as in most cases the material is only indiscernibly effected. The force applied in a hardness test correlated either with the depth of indent or with area of indent provides a measurement of hardness. Typically the properties and usefulness of the material is not compromised. Microhardness testing is the best example of a nondestructive hardness test. Some of the more common NDT test types are described below.

Eddy Current Testing

Eddy Current testing utilizes the principal of “electromagnetism” as the basis for conducting examinations. In eddy current testing, a current is introduced to the material. Changes in the current based on the material provide valuable workpiece information such as flaws and surface cracks. Eddy current testing can also be used to determine material hardness as well as material and coating thickness determination.

Rebound Testing

Rebound testing utilizes the Leeb Principle. In this method, an impact device uses a spring to propel an impact body through a guide tube toward the test piece. As it travels toward the test piece, a magnet contained within the impact body generates a signal in a coil encircling the guide tube. After the impact, it rebounds from the surface inducing a second signal into the coil. The instrument calculates the hardness value using the ratio of the voltages and analyzes their phases to automatically compensate for changes in orientation. Since the device is electronic in nature, most Leeb instruments are designed to automatically convert from the Leeb number to a more conventional hardness scale. By using a variety of different conversions to suit the different materials, a wide range of metallic parts can be tested. The main limitations are that the parts must have a good finish and a minimum weight of 5kg. Leeb testers are portable and can be used at different angles as long as they are perpendicular to the test surface.

Ultrasonic Contact Impedance

Ultrasonic Contact Impedance or UCI testing utilizes a diamond indenter similar to that used in a classic Vickers Microhardness test. While conventional Vickers requires optical evaluation of the area of an indent, the UCI method electronically detects by a shift of an ultrasonic frequency. UCI testers use a spring to apply approximately a 5kg force to a Vickers indenter that is attached to the end of a resonating rod. As the resonating rod and Vickers indenter penetrate the test sample a frequency shift will occur in the rod. The amount of the frequency shift is measured and can be related to the depth of penetration of the Vickers indenter into the sample. The results are electronically converted to other hardness scales such as Vickers and Rockwell. UCI instruments can test a wide variety of materials using different conversions as long as the test sample has a smooth surface and is at least 0.5in thick.

NDT is a valuable and growing tool in the evaluation and maintenance of materials. In our rapidly changing and highly mobile environment, dependable, efficient, and effective tools are needed to meet the quality demands of the manufacturing, R&D, and inspection sectors. NDT technologies will continue to play a major role in these areas.

Leave a Reply

Your email address will not be published. Required fields are marked *

This site uses Akismet to reduce spam. Learn how your comment data is processed.

Optimize Your Sectioning
Buehler an ITW Company
Buehler Products

Applications of Metamaterials

With Prof. Lorenzo Valdevit

An overview of the definitions and classes of metamaterials will be provided with a specific emphasis to the applications as lightweight structural materials. The various features of structural metamaterials will be discussed as well as the role of metal additive manufacturing in enabling the scale of these materials. Future pathways to the implementation of these unique materials will be presented.

Applications of Light Metals

With Dr. Carl Söderhjelm

The lecture will first review the prototypical structures and identifying properties of various industrially relevant light metals. Then, several case studies will be presented to demonstrate the novel use of these materials in light weighting across different fields. The lecture will conclude with emerging materials and tools to design them.

Additive Manufacturing Overview

With Mr. Brandon Fields

The field of metal additive manufacturing will be discussed with a highlight to the variety of technologies currently in use and identify the industry leading techniques. The core principals of each will be presented along with comparisons and use cases for each.

Powder Metallurgy Versus Conventional Processing

With Prof. Diran Apelian or Dr. Ben MacDonald

Powder metallurgy as a class of processing technologies will be covered with an emphasis to the key differentiations with conventional processing. The implication of critical solidification parameters including cooling rate will be reviewed as they affect the refinement of microstructures and the presence of metastable structures. Traditional consolidation approaches to creating bulk parts will be discussed as well as the use of metal powder as a feedstock to additive manufacturing.

The Linkage of Processing Structure Properties

With Dr. Ben MacDonald

This lecture will serve to established and review the core metallurgical principles that are essential to understanding materials as a system. With an overview of the hierarchical structural features of metals, fundamentals of solidification, wrought processing, and heat treatment, the interconnected relationships of processing, structure, and properties will be established.

Current Trends in Light Weighting of Structural Materials

With Prof. Diran Apelian

This lecture will serve as a motivation for the course with emphasis on current trends in light weighting of structural materials. Global context to the need for light weighting will be provided as it is critical to a variety of fields from aerospace to the electrification of transportation. Paths forward will be proposed, specifically the unique potential of metal additive manufacturing to accomplishing these goals. This lecture will conclude by introducing the structure of the lectures that will be presented in the course.